RESINA RI 301

RESINA RI 301

PURE, FLUID, SOLVENT-FREE EPOXY RESINS

Transparent, solvent free epoxy resin; high fluidity (500-800 cps), modified with reactive diluent.

Technical Documents
Technical characteristics U.M.
Epoxy equivalent weight ASTM D-1652182 - 188g/eq
Colour (Gardner) ASTM D-15443
Viscosity at 25 °C ISO 9371500 - 700cP
Flash point ISO 2719135°C
Density at 25 °C ISO 16751,14Kg/dm3
A+B mixture ratio with:
    HP 150
    HP 157
    HI 362
    H 22
    H 45
    H 92

100 + 45
100 + 60
100 + 25
100 + 50
100 + 60
100 + 30

Pour the hardening agent in the resin and blend at slow speed for 3’ – 5’ using drill with helix/spiral to reduce air inlet as much as possible; during this operation, scrape also the bottom and the sides of the container.
Three essential rules are valid for all bi-component systems: weigh well, carefully mix bottom and walls,
observe times of use.

The reaction between the two components starts immediately after mixture: processing time is therefore
limited and depends on the temperature. The table shows RI 301 times at 20 °C together with different types of hardening agents.

Resin + hardening agentPot life at + 20 °C
RI 301 + HP 15035 - 40'
RI 301 + HP 15750 - 55'
RI 301 + HI 36235 - 40'
RI 301 + H 2230 - 35'
RI 301 + H 4555 - 60'
RI 301 + H 925'

Minimum hardening temperature = + 10 °C.
At 20 °C the product hardens in 8 hours; complete h ardening occurs after 7 days.

RI 301 is available in 1 kg – 5 kg – 10 kg – 20 kg packages

The product remains unaltered for at least a year if stored in a place at a temperature between +10°C and +30°C in its original sealed containers.

  • Synthetic concrete screed binding agents;
  • Binding agents for multi-layered floors with ceramic quartz finishing;
  • Impregnation or pressure injection structural strengthening;
  • Structural gluing injections of cracks and clefts in building materials;
  • Injection gluing of marble, ceramic and wooden floors in case of foundation ungluing which may cause voids.