Thixotropic adhesive paste based on solvent-free epoxy resins and hardened with modified aliphatic and cyclo-aliphatic polyamines mixed with mineral fillers.
It can be spatula applied vertically and in the intrados.
| Property | Value |
|---|---|
| Compression strength (UNI EN 12190) | > 80 MPa |
| Bending strength (UNI EN 12190) | > 45 MPa |
| Elastic modulus (UNI EN 13412) | 9000 MPa |
| Adhesion to dry concrete (ISO 4624) | > 4.0 MPa |
| Adhesion to humid concrete (ISO 4624) | > 2.0 MPa |
| Slant shear strength at 50° | 58 MPa |
| Slant shear strength at 60° | 64 MPa |
| Slant shear strength at 70° | 70 MPa |
| Adhesion to wood (pine, larch, chestnut, oak) | 2.5 – 3.7 MPa |
| Linear shrinkage (UNI EN 12617-1) | < 0.1 mm/m |
| Linear thermal shrinkage (UNI EN 1770) | 3.9∙10⁻⁵ °C⁻¹ |
| Glass transition point | ca. 60 °C |
| Density | 1.95 kg/dm³ |
| A + B mixture ratio | 100 + 6 |
Preparation of the support
Smoothing: the surfaces to be coated must be compact, clean (no oil or fat), dry (support damp <5%) and mortar grout and crumbly part-free. For better adhesion the surface must be slightly roughened with sandblasting or sanding; then remove any sign of dust or dirt using an exhauster.
Gluing and mending: in case of gluing or repair of a cracked element, we recommend opening up the crack as much as possible by possibly moving away the parts to be glued (in case of doorstones, steps or non-movable parts); remove the crumbling parts with abrasive disk, brush or scraper and thoroughly clean with vacuum cleaner or compressed air.
Metals must be sanded to SA 2,5 degree or alternatively grinded or vigorously cleaned with metal brush and then treated with
RESICOLOR 425 specific primer.
The presence of water has a negative effect on adhesion. Wet
foundations must be dried up as much as possible using air or, better, using gas flame.
Preparation of the product
Pour component B into component A and blend at slow speed for 3’ – 5’ using drill with helix/spiral to reduce air inlet as much as possible; during this operation, scrape also the bottom and the sides of the container.
Application
Smoothing: apply the material with a steel or nylon palette knife.
Gluing and mending: apply the material on the gluing surface using a knife or trowel in 2 to 4 mm thicknesses based on the surfaces to be glued/joined and moderately press the elements until some adhesive comes out from the sides, then make sure they remain pressed/places until hardening (6 hours at 20 °C).
Notes
Packages are weight pre-measured out: fully use all components A and B. If you wish to divide the package, products must be weighed by respecting the A+B ratio on the label and must not be weighed out based on the volume.
By pouring B component into A component, the hardening reaction starts: following mixture the time available is limited and it depends on the temperature.
| Temperature | Pot-life | Hardening |
|---|---|---|
| 10°C | 70 min | 9½ h |
| 20°C | 50 min | 5 h |
| 30°C | 35 min | 4 h |
| 40°C | 10 min | 3 h |
Full hardening after 7 days.
For application at low temperature or even if a faster reaction time is requested, it’s available the
rapid hardener RESICOL 100 Rapido Comp. B.
Consumption
Gluing and smoothing: approx. 2 kg/m² for a layer 1 mm thick.
Packaging and stocking
RESICOL 100 is available in 1kg and 5 kg packages (A + B component).
If stored in its original and sealed package, the products remains unaltered for 18 months if kept in
environments with a temperature between 10 and 30 °C.